TPU Hot Melt Adhesive Film for Waterproof Outdoor Jackets and Rainwear
TPU Hot Melt Adhesive Film for Waterproof Outdoor Jackets and Rainwear
TPU adhesive film for waterproof outdoor jackets and rainwear is a flexible heat-activated bonding film for coated outdoor fabric, storm flaps, cuffs, hems and local reinforcement areas. It supports soft garment component bonding without claiming that the film alone creates waterproof performance.
| Material | TPU / Modified TPU |
|---|---|
| Thickness | 0.025-0.30 mm reference; confirm by fabric and bonding position |
| Width | 54 inch reference; custom slitting available |
| Appearance | Transparent / Translucent |
| Liner | Release paper / release film / liner-free by grade |
| Supply Form | Roll / slit roll / sheet / die-cut piece |
| Application | Waterproof jackets, rainwear, coated outdoor fabrics, seam and trim bonding |
| Sample Grade Direction | ZF-6235 / ZF-7608 / ZF-5180 |
Product Categories
Product Fit
This TPU hot melt adhesive film is positioned for waterproof outdoor jackets, rainwear and coated garment structures where the bonded area must stay flexible after bending, wearing and washing trials. It can be evaluated for seam-related bonding, flap reinforcement, cuff and hem areas, reflective tape backing and selected waterproof textile laminations.
The film should be tested on the real fabric, coating and lamination equipment before bulk order. Water resistance, peel strength, flexing, washing and appearance after cooling are the main checks for this product direction.
Key Features
- Flexible TPU bonding layer for soft outdoor garment structures.
- Suitable for roll, slit roll, sheet and die-cut supply according to production layout.
- Can be supplied with release paper, release film or liner-free handling by grade and process.
- Useful for sample trials where coated fabric compatibility, edge lifting and hand feel must be checked.
Recommended Applications
| Application Area | Typical Product / Bonding Position | What To Confirm |
|---|---|---|
| Waterproof jackets and rainwear | Seam-adjacent bonding, storm flap layers, hood and pocket reinforcement | Water pressure requirement, fabric coating, edge lifting, stitch area appearance and washing test. |
| Outdoor garment cuffs and hems | Cuff edge, hem fold, sleeve opening and local reinforcement strip | Hand feel, stretch recovery, glue mark risk and bending after cooling. |
| Reflective tape or trim backing | Reflective strip backing, decorative tape, zipper flap or label area | Tape backing material, surface treatment, peel strength and heat mark tolerance. |
| Coated outdoor textile panels | Nylon, polyester or TPU-coated fabric lamination trials | DWR or coating compatibility, bubbling, shrinkage and final water-resistance test method. |
Suitable Bonding Materials
Typical trial materials include polyester fabric, nylon fabric, coated outdoor fabric, TPU membrane, selected PU-coated textiles, reflective tape backing and soft reinforcement fabrics. DWR-treated, silicone-treated or heavily coated surfaces should be tested before bulk production because surface finish can strongly affect adhesion.
Selection Notes Before Sampling
| Selection Item | What The Buyer Should Check |
|---|---|
| Fabric and coating | Confirm fiber type, coating system, DWR finish and whether the adhesive contacts fabric, membrane, tape backing or coating layer. |
| Thickness choice | Use thinner film for softer hand feel; consider thicker film when the fabric is textured or needs stronger wet-out. |
| Liner and converting | Choose release paper, release film or liner-free handling based on slitting, die cutting, positioning and operator handling. |
| Outdoor durability test | Define water pressure, washing, flexing, aging and peel test requirements before sample selection. |
| Appearance control | Check heat marks, strike-through, yellowing, edge lift, shrinkage and flatness after cooling. |
Sample Grade Selection
| Public Code | Material | Melting Point Reference | Starting Service Conditions | Temperature Range | Sample Direction |
|---|---|---|---|---|---|
| ZF-6235 | TPU | 95-100 C | 0.1-0.4 MPa, 160-200 C, 10-20 s | -40 C to 100 C | Outdoor clothing labels, waterproof zipper and higher-temperature textile confirmation. |
| ZF-7608 | TPU | 85 C | 0.1-0.4 MPa, 110-130 C, 10-20 s | -30 C to 85 C | Fabric bonding trials where a lower starting temperature may help protect garment surface. |
| ZF-5180 | TPU | 75-80 C | 0.1-0.4 MPa, 80-110 C, 5-20 s | -20 C to 80 C | Lower-temperature textile or coated-fabric sample direction when heat marks are a concern. |
Basic Processing Guide
Start with clean, dry fabric and confirm the real interface temperature, not only the machine display. For TPU outdoor garment trials, common starting directions are around 110-150 C, 0.2-0.5 MPa and 8-20 seconds, then adjust by fabric thickness, coating, equipment and required test method. Use the model-specific table above when a public sample code is selected.
Let samples cool and condition before peel, water pressure, washing, flexing or aging checks. Change one process variable at a time so the factory can identify whether failure comes from heat, pressure, dwell time, coating compatibility or film thickness.
Customization And Sample Support
For sample recommendation, share the fabric type, coating or membrane structure, target bonding position, required width or die-cut shape, processing equipment, working temperature limit and final test method. VELNORA can use this information to suggest a starting TPU film direction for rainwear and waterproof outdoor garment trials.
Quality Control Summary
Outdoor garment samples should be checked for film appearance, thickness and width, liner condition, melt behavior, bonding trial result, edge lifting, bubbling, glue marks and storage condition. Water-resistance or washing performance should be confirmed by the buyer’s own finished-garment test standard.
FAQ
Can this film make a jacket waterproof by itself?
No. The adhesive film is one bonding layer inside the garment structure. Waterproof performance depends on fabric, coating, seam design, tape or lamination structure, processing and final water-pressure testing.
Which grade should I request first?
For outdoor jackets and rainwear, ZF-6235, ZF-7608 and ZF-5180 can be discussed as starting sample directions. Final selection depends on the real coated fabric, heat sensitivity, hand feel and test requirement.
Can it be supplied as narrow slit rolls or die-cut pieces?
Yes. Roll, slit roll, sheet and die-cut supply can be reviewed according to seam width, flap width, trim shape and production equipment.
What should be reviewed before rainwear production?
Check peel strength, water pressure or leakage requirement, washing, flexing, heat aging, appearance, glue marks and edge lift on the actual finished garment structure.
Related Products
- TPU Hot Melt Adhesive Film
- Low Temperature TPU Hot Melt Adhesive Film for Heat-Sensitive Materials
- TPU Hot Melt Adhesive Film for Elastic Apparel and Seamless Garments
- PES Hot Melt Adhesive Film
Sample And Inquiry Guidance
Send the outdoor fabric structure, coating type, bonding position, target width, machine type and testing standard when requesting samples. The product page uses global inquiry buttons, so no manual CTA buttons are inserted inside this description.
Certified Quality Systems & Test Reports
VELNORA operates under ISO 9001 quality management and ISO 14001 environmental management systems. Third-party test reports for REACH, RoHS / halogen, California Proposition 65, VOC, organotin and phthalates are available for buyer review on request.
ISO 9001 & ISO 14001 certified. REACH, RoHS, Prop 65, VOC and other test reports on request.
ISO 9001 Quality Management
ISO 14001 Environmental Management
REACH Report
RoHS / Halogen Report
California Prop 65 Report
VOC Report
Organotin Report
Phthalates Report